Aluminium manufacturer production process for aluminum slug
Our Aluminum Slugs can be availed at industrial leading price,which are manufactured from high grade quality raw materials. These are widely known for its durability and quality. Smelting for aluminum slug
This stage starts by loading furnaces F1th ,F2th with 30MT each of raw aluminum (alloy AA1070, purity 99,7%),Once production cycle is established following Ration will be based on percentages of 30% in-plant scrap and 70% ingots (raw aluminum).. To ensure a consistent metal quality with low oxide levels, the molten aluminum is degassed, refined and filtered before it enters the casting wheel.
Continuous casting and hot-cold rolling for aluminum slug
The melt is poured into the strip casting wheel, which rotates at a speed of 6 meters/min. A strip of 220 mm wide by 20 mm thick is formed between the grooved periphery of the strip casting wheel and the endless steel belt. The strip casting wheel is water cooled.. Each coil is properly identified with heat number, weight, thickness and then is moved to a natural cooling area. Hot-Cold Rolling time using furnace F1th and F2th is 6-8 hours.
Cold Lamination/Rolling for aluminum slug
Following, coil’s thickness is reduced accordingly to customers specifications by means of cold rolling. This stage is very important because it is precise to keep a close control on specifications in order to fill international standards norms, which aloud a maximum tolerance 0,05 mm.
Stamping for aluminum slug
This stage counts with four stamping presses, each one has a decoiler where a coil is mounted. Strip is fed into the press, and at the center of it is located the die.. The strip is lubricated while it is being punched. Cut slugs fall on a conveyor belt which takes them into a holding hopper and then into rectangular Mould . Punched strips (scrap) are then cut in pieces which are then compacted before sent back to the furnace. In this process we get about 50% of slugs for each Ton of punched strip. Annealing Treatment for aluminum slug
This stage counts with Five annealing furnaces, electrically controlled. The aim of annealing is to produce a material with minimum strength, maximum ductility and soft temper. slugs are placed inside an annealing furnace and temperature is rise to 520 ºC for Four-Six hours, With this we obtain a Brinell hardness of 16 a 21 HB.
Surface Finish for aluminum slug
The surface of the slugs is treated in order to obtain a rough,This is done by placing the slugs inside of mechanically operated gyratory drums. Slugs hit each other hence roughening the surface. Final customer needs this roughness in order to apply a lubricant necessary for cold extrusion.Surface treatment is Tumbling and Shot Blasting.
Packing and shipping for aluminum slugs
packaging:with standard or as your request
shipping: 7~25 working days